Filament Compozit Anisoprint

Name: Filament Compozit Anisoprint
Brand: Anisoprint
SKU: FIL-ANISOPRINT
Price: 1145 RON
Availability: InStock

1.195,⁰⁰ RON (Reducere 4%)

1.145,⁰⁰ RON

Prețul include TVA, nu include transportul și se aplică pentru comenzi online. Pentru achiziții publice, comenzi directe, etc. prețurile pot diferi.

Stoc: 1

SKU	Filament Compozit Anisoprint	Preț (inclusiv TVA)	Pret vechi	Cantitate	Stoc
FIL-ANISOPRINT-CBF	750m CBF - Fibre compozit de bazalt	1.145,⁰⁰ RON	1.195,⁰⁰ RON		1
FIL-ANISOPRINT-CCF	750m CCF - Fibre compozit de carbon	1.795,⁰⁰ RON	1.895,⁰⁰ RON		N/A

Cod produs - SKU: FIL-ANISOPRINT

Descriere

Anisoprint CCF (Composite Carbon Fiber) and CBF (Composite Basalt Fiber) are a composite reinforcing fibers in the form of a tow made of thousands of ultrathin carbon or basalt monofilaments, impregnated with a special polymer composition ensuring high-quality adhesion between the polymers and the fiber. Composite fiber is used to reinforce the plastic during fabrication of the part.

CCF-1.5K Carbon Composite Fiber Properties

30 times stiffer and stronger than normal plastic
Strength-to-weight ratio is more than 5 times higher than for 2024-T351 Aluminum
Stiffness-to-weight ratio is more than 5 times higher than for 2024-T351 Aluminum
7 times lighter than steel and strong as stainless steel

Effective Diameter, mm	VF, %	Elastic Modulus, GPa	Tensile Strength, MPa
0.35	60	149	2206

CBF

15 times stiffer and stronger than normal plastic
Strength-to-weight ratio is more than 2 times higher than for 2024-T351 Aluminum
5 times lighter than steel and strong as stainless steel

Dual-matrix Composite Properties

Parameter	CCF-1.5K-PETG
Density, g/cm³	1.4
Tensile modulus in fiber direction, GPa	64
Poisson ratio 31	0.36
Tensile ultimate stress in fiber direction, MPa	860
Compressive ultimate stress in fiber direction, MPa	290
Flexural Strength along axis 1 under bending in plane 1-3, MPa	520

NOTE:

The test data was obtained applying standard and nonstandard specific test methods. All the test results are preliminary but not final and should be considered as reference. The data cannot be used for design and analysis of certain parts. Anisoprint provides no warranties on the use of this data.